Corrosion behavior study of AZ91 magnesium alloy coated with methyltriethoxysilane doped with cerium ions

2019/6/5

The present work aims to investigate the corrosion behavior of AZ91 magnesium alloy treated with a 4% (v/v) Methyltriethoxysilane (MTES) alcohol solution, with and without an alkaline pretreatment. The corrosion resistance was assessed by electrochemical impedance spectroscopy (EIS) and current densities were monitored by potentiodynamic polarization curves during immersion in a 0.1?M Na2SO4 solution. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used to perform a surface analysis. The electrochemical results showed an improvement of anticorrosion properties of AZ91. Furthermore, alkaline pretreatment enhances adhesion between silane film and substrate surface. This can be attributed to a surface enrichment in hydroxyl groups after the alkaline step, which increases formation of Si–O–Mg covalent bonds. The addition of Ce(NO3)3 to the MTES bath was evaluated, and it was found that the electrochemical response depends on the cerium ions concentration used. It was shown that the addition of 6.0?×?10?5?M of Ce(NO3)3 to a MTES bath improves corrosion resistance. Higher concentration of cerium ions lead to destabilizing the siloxane network, decreasing the efficiency of the silane coatings.